______________________________________________________________________ |Product Name |Poly-Flex|Poly-Flex |Poly-Flex |Poly-Flex |Poly-Flex | |________________|_________|__________|__________|__________|__________| |Polymer Type |HDPE |HDPE |HDPE |HDPE |HDPE | |________________|_________|__________|__________|__________|__________| |Roll Width |6.85/305 |6.85/244 |6.85/183 |6.85/122 |6.85/91 | |Roll Length |(22.5/ |(22.5/800)|(22.5/600)|(22.5/400)|(22.5/300)| | m(ft) | 1000) | | | | | |________________|_________|__________|__________|__________|__________| |Thickness |0.5 |0.75 |1.0 |1.5 |2.0 | |ASTM D751 |(45) |(65) |(90) |(60) |(80) | |mm(mils) | | | | | | |________________|_________|__________|__________|__________|__________| |Density |0.940 |0.940 |0.940 |0.940 |0.940 | |ASTM D1505 | | | | | | |________________|_________|__________|__________|__________|__________| |Tensile Strength| | | | | | |ASTM D638 | | | | | | |kN/m(lb/in) | | | | | | |Yield |7.9 (80) |11.4 (120)|15.8 (160)|23.7 (135)|31.5 (180)| |Elongation % |13 |13 |13 |13 |13 | |Break |14.0 (27)|21.0 (41) |28.0 (54) |42.0 (240)|56.1 (320)| |Elongation% |700 |700 |700 |700 |700 | |________________|_________|__________|__________|__________|__________| |Puncture |0.12 (14)|0.18 (21) |0.24 (28) |0.36 (81) |0.48 (108)| |Resistence | | | | | | |FTMS 101C | | | | | | |Method 2065 | | | | | | |kN (lbs) | | | | | | |________________|_________|__________|__________|__________|__________| | |Tear Resistence |0.06 |0.09 |0.12 |0.19 (42) |0.25 (56) | |ASTM D1004 | | | | | | | kN (lbs) | | | | | | |________________|_________|__________|__________|__________|__________| |Low Temp.Brittle|-70 (-94)|-70 (-94) |-70 (-94) |-70 (-94) |-70 (-94) | | | |ASTM D746 C(F) |(40) |(60) |(81) | | | |________________|_________|__________|__________|__________|__________| |Seam Strength | | | | | | |ASTM D 4437 | | | | | | | |kN/m (lbs/in) | | | | | | |Shear- Fusion |7.0 (40) |10.5 (60) |14.2 (81) |21.2 (121)|28.4 (162)| |Shear- Extrusion|7.0 (31) |10.5 (45) |14.2 (63) |21.2 (121)|28.4 (162)| |________________|_________|__________|__________|__________|__________| |Peel- Fusion |5.4 (27) |7.9 (39) |11.0 (54) |16.5 (94) |22.1 (126)| |Peel- Extrusion |4.7 |6.8 |9.5 |14.2 (81) |18.9 (108)| |________________|_________|__________|__________|__________|__________| |Carbon Black |2 |2 |2 |2 |2 | |ASTM D 1603 (%) | | | | | | |________________|_________|__________|__________|__________|__________| |Envir. Stress |200 |200 |200 |200 |200 | |Crack Resist. | | | | | | |ASTM 5397 Hours | | | | | | |________________|_________|__________|__________|__________|__________| |Manufact. |LL,LC,TL,|LL,LC,TL, |LL,LC,TL, |LL,LC,TL, |LL,LC,TL, | |Suggested |DL,LPL,CL|DL,LPL,CL,|DL,LPL,CL,|DL,LPL,CL,|DL,LPL,CL,| |Applications |SIL,SIC |SIL,SIC |SIL,SIC |SIL,SIC |SIL,SIC | |________________|_________|__________|__________|__________|__________|
______________________________________________________________________ |Product |Poly-Flex|Poly-Flex |Poly-Flex |Poly-Flex |Poly-Flex | |Name | |Roughened |Roughened |Roughened |Roughened | |________________|_________|__________|__________|__________|__________| |Polymer Type |HDPE |HDPE-T |HDPE-T |HDPE-T |HDPE-T | |________________|_________|__________|__________|__________|__________| |Roll Width |6.85/76 |6.85/ |6.85/122.0|6.85/106.7|6.85/76.2 | |Roll Length |(22.5/ |137.2 |(22.5/400)|(22.5/350)|(22.5/250)| | m(ft) | 250) |(22.5/450)| | | | |________________|_________|__________|__________|__________|__________| |Thickness |2.5 (100)|1.0 |1.25 |1.5 |2.0 | |ASTM D751 | | | | | | |mm(mils) | | | | | | |________________|_________|__________|__________|__________|__________| |Density |0.940 |0.940 |0.940 |0.940 |0.940 | |ASTM D1505 | | | | | | |________________|_________|__________|__________|__________|__________| |Tensile Strength| | | | | | |ASTM D638 | | | | | | |kN/m(lb/in) | | | | | | |Yield |39.4(225)|13.7 (78) |13.7 (78) |20.5 (117)|27.3 (156)| |Elongation % |13 |13 |13 |13 |13 | |Break |68.3(390)|10.5 (60) |13.1 (75) |15.8 (90)|19.3 (110)| |Elongation% |700 |200 |200 |200 |200 | |________________|_________|__________|__________|__________|__________| |Puncture |0.60 |0.20 |0.20 |0.33 |0.40 | |Resistence |(135) |(45) |(48) |(75) |(90) | |FTMS 101C | | | | | | |Method 2065 | | | | | | |kN (lbs) | | | | | | |________________|_________|__________|__________|__________|__________| | |Tear Resistence |0.31 (70)|0.11 (24) |0.13 (30) |0.18 (40) |0.22 (50) | |ASTM D1004 | | | | | | | kN (lbs) | | | | | | |________________|_________|__________|__________|__________|__________| |Low Temp.Brittle|-70 |-70 |-70 |-70 |-70 | | | |ASTM D746 C(F) |(94) |(94) |(94) |(94) |(94) | |________________|_________|__________|__________|__________|__________| |Seam Strength | | | | | | |ASTM D 4437 | | | | | | | |kN/m (lbs/in) | | | | | | |Shear- Fusion |35.4(202)|12.3 (70) |15.2 (87) |18.4 (105)|24.5 (140)| |Shear- Extrusion|35.4(202)|12.3 (70) |12.3 (87) |18.4 (105)|24.5 (140)| |________________|_________|__________|__________|__________|__________| |Peel- Fusion |27.5(157)|8.2 (47) |10.2 (58) |12.3 (70) |16.5 (94) | |Peel- Extrusion |23.7(135)|8.2 (47) |10.2 (58) |12.3 (70) |16.5 (94) | |________________|_________|__________|__________|__________|__________| |Carbon Black |200 |200 |200 |200 |200 | |ASTM D 1603 (%) | | | | | | |________________|_________|__________|__________|__________|__________| |Envir. Stress |LL,LC,TL,|LL,LC,TL, |LL,LC,TL, |LL,LC,TL, |LL,LC,TL, | |Crack Resist. |DL,LPL, |DL,LPL,CL,|DL,LPL,CL,|DL,LPL,CL,|DL,LPL,CL,| |ASTM 5397 Hours |CL,SIL, |SIL,SIC |SIL,SIC |SIL,SIC |SIL,SIC | | |SIC | | | | | |________________|_________|__________|__________|__________|__________| |Manufact. | | | | | | |Suggested | | | | | | |Applications | | | | | | |________________|_________|__________|__________|__________|__________|